| 布氏硬度 HB | 洛氏硬度 | 维氏 硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 86.6 | 70.0 | 1037 | 78.5 | 55.0 | 599 | ||
| 86.3 | 69.5 | 1017 | 78.2 | 54.5 | 589 | ||
| 86.1 | 69.0 | 997 | 77.9 | 54.0 | 579 | ||
| 85.8 | 68.5 | 978 | 77.7 | 53.5 | 570 | ||
| 85.5 | 68.0 | 959 | 77.4 | 53.0 | 561 | ||
| 85.2 | 67.5 | 941 | 77.1 | 52.5 | 551 | ||
| 85.0 | 67.0 | 923 | 76.9 | 52.0 | 543 | ||
| 84.7 | 66.5 | 906 | 76.6 | 51.5 | 534 | ||
| 84.4 | 66.0 | 889 | 501 | 76.3 | 51.0 | 525 | |
| 84.1 | 65.5 | 872 | 494 | 76.1 | 50.5 | 517 | |
| 83.9 | 65.0 | 856 | 488 | 75.8 | 50.0 | 509 | |
| 83.6 | 64.5 | 840 | 481 | 75.5 | 49.5 | 501 | |
| 83.3 | 64.0 | 825 | 474 | 75.3 | 49.0 | 493 | |
| 83.1 | 63.5 | 810 | 468 | 75.0 | 48.5 | 485 | |
| 82.8 | 63.0 | 795 | 461 | 74.7 | 48.0 | 478 | |
| 82.5 | 62.5 | 780 | 455 | 74.5 | 47.5 | 470 | |
| 82.2 | 62.0 | 766 | 449 | 74.2 | 47.0 | 463 | |
| 82.0 | 61.5 | 752 | 442 | 73.9 | 46.5 | 456 | |
| 81.7 | 61.0 | 739 | 436 | 73.7 | 46.0 | 449 | |
| 81.4 | 60.5 | 726 | 430 | 73.4 | 45.5 | 443 | |
| 81.2 | 60.0 | 713 | 424 | 73.2 | 45.0 | 436 | |
| 80.9 | 59.5 | 700 | 418 | 72.9 | 44.5 | 429 | |
| 80.6 | 59.0 | 688 | 413 | 72.6 | 44.0 | 423 | |
| 80.3 | 58.5 | 676 | 407 | 72.4 | 43.5 | 417 | |
| 80.1 | 58.0 | 664 | 401 | 72.1 | 43.0 | 411 | |
| 79.8 | 57.5 | 653 | 396 | 71.8 | 42.5 | 405 | |
| 79.5 | 57.0 | 642 | 391 | 71.6 | 42.0 | 399 | |
| 79.3 | 56.5 | 631 | 385 | 71.3 | 41.5 | 393 | |
| 79.0 | 56.0 | 620 | 380 | 71.1 | 41.0 | 388 | |
| 78.7 | 55.5 | 609 | 375 | 70.8 | 40.5 | 382 | |
Tebụl mgbanwe uru nke ihe ígwè ferrous siri ike
| 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 370 | 70.5 | 40.0 | 377 | 269 | 28.0 | 274 | |
| 365 | 70.3 | 39.5 | 372 | 266 | 27.5 | 271 | |
| 360 | 70.0 | 39.0 | 367 | 263 | 27.0 | 268 | |
| 355 | 38.5 | 362 | 260 | 26.5 | 264 | ||
| 350 | 38.0 | 351 | 257 | 26.0 | 261 | ||
| 345 | 37.5 | 352 | 254 | 25.5 | 258 | ||
| 341 | 37.0 | 347 | 251 | 25.0 | 255 | ||
| 336 | 36.5 | 342 | 248 | 24.5 | 252 | ||
| 332 | 36.0 | 338 | 245 | 24.0 | 249 | ||
| 327 | 35.5 | 333 | 242 | 23.5 | 246 | ||
| 323 | 35.0 | 329 | 240 | 23.0 | 243 | ||
| 318 | 34.5 | 324 | 237 | 22.5 | 240 | ||
| 314 | 34.0 | 320 | 234 | 22.0 | 237 | ||
| 310 | 33.5 | 316 | 232 | 21.5 | 234 | ||
| 306 | 33.0 | 312 | 229 | 21.0 | 231 | ||
| 302 | 32.5 | 308 | 227 | 20.5 | 229 | ||
| 298 | 32.0 | 304 | 225 | 20.0 | 226 | ||
| 294 | 31.5 | 300 | 222 | 19.5 | 223 | ||
| 291 | 31.0 | 296 | 220 | 19.0 | 221 | ||
| 287 | 30.5 | 292 | 218 | 18.5 | 218 | ||
| 283 | 30.0 | 289 | 216 | 18.0 | 216 | ||
| 280 | 29.5 | 285 | 214 | 17.5 | 214 | ||
| 276 | 29.0 | 281 | 211 | 17.0 | 211 | ||
| 273 | 28.5 | 278 | |||||
Rịba ama:
1. Ike siri ike nke Brinell: A na-ejikarị ya atụ ihe siri ike nke ihe e ji kpụọ ihe, ihe e ji akpụ ihe, akụkụ ígwè na-abụghị ferrous, billets na-ekpo ọkụ na akụkụ ndị a na-akpọ annealed. Oke nha ya bụ ≥HB450.
2. Ike Rockwell: A na-ejikarị HRA eme ihe maka ihe nlele siri ike iji tụọ ike elu nke ihe na elu ndị nwere ike karịrị HRC67, dị ka carbide simenti, ígwè nitrided, wdg. Oke nha bụ HRA>70. A na-ejikarị HRC atụ ike nke akụkụ ígwè (dị ka ígwè carbon, ígwè ngwaọrụ, ígwè alloy, wdg) mgbe emechara ma ọ bụ mee ka ọ dị ọkụ. Oke nha bụ HRC20~67.
3. Ike Vickers: a na-eji ya atụ ike nke akụkụ dị gịrịgịrị na akụkụ efere ígwè, a pụkwara iji ya tụọ ike nke akụkụ ndị siri ike dị n'elu dịka kaburizing, cyaniding, na nitriding.
Oge ozi: Eprel-07-2024